Flame Retardant
- Halogen Flame Retardant
- Phosphorus Flame Retardant
- Nitrogen Flame Retardant
- Silicon Flame Retardant
- Aluminum-Magnesium Flame Retardant
- Antimony Flame Retardant
- Boron Flame Retardant
- Expandable Graphite
- MOF Flame Retardant
- Nano Flame Retardant
- Hyperbranched Polymer Flame Retardant
-
Functional Flame Retardant
- Composite Flame Retardant for PA
- Composite Flame Retardant for PP
- Composite Flame Retardant for PBT
- Composite Flame Retardant for PVC
- Composite Flame Retardant for PU
- Composite Flame Retardant for Silicone Rubber
- Composite Flame Retardant for Epoxy Resin
- Composite Flame Retardant for TPU
- Composite Flame Retardant for TPE
- Cotton Durable Flame Retardant
- Polyester Durable Flame Retardant
- Semi-durable Flame Retardant
- Non-durable Flame Retardant
- Others
- Smoke Suppressant
- Flame Retardant Polymer
- Flame Retardant Masterbatch
ZIF-8
Inquiry| Catalog | ACM59061539-1 |
| CAS | 59061-53-9 |
| Structure | ![{[CurrentData.Name]}](https://resource.alfa-chemistry.com/structure/59061-53-9.gif) |
| Synonyms | 2-Methylimidazole zinc salt |
| Molecular Weight | 227.58 |
| Molecular Formula | C8H10N4Zn |
| Appearance | Off-white Powder |
| Storage | Store at room temperature or 4 °C in dry-state. Recommend to be activated at 150 ℃ in a vacuum oven for 3 hours before use |
| Ligand | 2-Methylimidazole (CAS: 693-98-1) |
| Metal Content | Zn |
| Particle Size | 100-400 nm, 300-600 nm, 0.6-1 μm, ~1 μm |
| Pore Size | 0.34 nm; 1.1 nm |
| Pore Volume | 0.66 cm³/g |
| Size | 200 nm; 500 nm; 1 µm; 5 µm |
| Specific Surface Area | 1500 m²/g (by BET) |
| Stability | Thermal stability: >400°C; Stable in air, aqueous and basic solution, not stable in acid solution |