Flame Retardant
- Halogen Flame Retardant
- Phosphorus Flame Retardant
- Nitrogen Flame Retardant
- Silicon Flame Retardant
- Aluminum-Magnesium Flame Retardant
- Antimony Flame Retardant
- Boron Flame Retardant
- Expandable Graphite
- MOF Flame Retardant
- Nano Flame Retardant
- Hyperbranched Polymer Flame Retardant
-
Functional Flame Retardant
- Composite Flame Retardant for PA
- Composite Flame Retardant for PP
- Composite Flame Retardant for PBT
- Composite Flame Retardant for PVC
- Composite Flame Retardant for PU
- Composite Flame Retardant for Silicone Rubber
- Composite Flame Retardant for Epoxy Resin
- Composite Flame Retardant for TPU
- Composite Flame Retardant for TPE
- Cotton Durable Flame Retardant
- Polyester Durable Flame Retardant
- Semi-durable Flame Retardant
- Non-durable Flame Retardant
- Others
- Smoke Suppressant
- Flame Retardant Polymer
- Flame Retardant Masterbatch
PC-specific high temperature flame retardant
InquiryApplication | It is more advantageous in the field of producing fully transparent polycarbon resin. Adding this product has very little impact on the transparency of the resin. It can basically maintain the light transmittance of the original resin and has almost no impact on the physical properties of the basic resin itself. |
Storage | Products are stored in cool, dry conditions. |
Carrier | PC |
Color | White |
Elongationat Break | ASTM D-638 214.68% |
Feature | The addition of this product has very little impact on the transparency of the resin, and can basically maintain the light transmittance of the original resin, and has almost no impact on the physical properties of the basic resin itself. After adding flame retardant, the glass transition temperature of the material basically does not change, especially the performance will be relatively stable. |
Flammability | UL94: V0 (3.2mm) |
Flexural Modulus | ASTM D-790 2285.76 MPa |
Flexural Strength | ASTM D-790 103.96 MPa |
Form | Granules |
Glass Transition Temperature | 152.63 ℃ |
Izod Impact-Notched | ASTM D-256 89.79 KJ/m2 |
Melt Flow Index | ASTM D-955 8.98 g/10min |
Notes | Directly add extrusion granulation. |
Tensile Strength | ASTM D-638 62.68 MPa |
Thermal Analysis | Weight loss 1% (347.3℃) Weight loss 5% (397.0℃) Weight loss 10% (416℃) Weight loss 50% (446℃) Weight loss 90% (517℃) |
Total Flame Retardant Content | 0.01 |
Transmittance | 0.8599 |
If the product of interest is not available in our catalog, please contact us to see if there is any relevant stock or other purchase channels.