Flame Retardant
- Halogen Flame Retardant
- Phosphorus Flame Retardant
- Nitrogen Flame Retardant
- Silicon Flame Retardant
- Aluminum-Magnesium Flame Retardant
- Antimony Flame Retardant
- Boron Flame Retardant
- Expandable Graphite
- MOF Flame Retardant
- Nano Flame Retardant
- Hyperbranched Polymer Flame Retardant
-
Functional Flame Retardant
- Composite Flame Retardant for PA
- Composite Flame Retardant for PP
- Composite Flame Retardant for PBT
- Composite Flame Retardant for PVC
- Composite Flame Retardant for PU
- Composite Flame Retardant for Silicone Rubber
- Composite Flame Retardant for Epoxy Resin
- Composite Flame Retardant for TPU
- Composite Flame Retardant for TPE
- Cotton Durable Flame Retardant
- Polyester Durable Flame Retardant
- Semi-durable Flame Retardant
- Non-durable Flame Retardant
- Others
- Smoke Suppressant
- Flame Retardant Polymer
- Flame Retardant Masterbatch
MIL-101 (Cr)-SO3H
Inquiry| CAS | 1331961-41-1 |
| Structure |  |
| Molecular Weight | 957.56 |
| Molecular Formula | C24H15Cr3O25S3.H2 |
| Appearance | Grey-green Powder |
| Storage | Store at room temperature or 4 °C in dry-state. Recommend to be activated at 150 ℃ in a vacuum oven for 3 hours before use |
| Ligand | Monosodium 2-Sulfoterephthalate (CAS: 19089-60-2) |
| Metal | Cr |
| Pore Size | Window size: 1.2-1.6 nm; pore size: 2.9-3.4 nm |
| Pore Volume | ~2.0 cm³/g |
| Size | 300-1 µm, Irregular |
| Specific Surface Area | 1800-2000 m²/g (by BET) |
| Stability | Thermal stability: > 300°C; Stable in air, aqueous, acid and basic solution (PH 1-12) |
If the product of interest is not available in our catalog, please contact us to see if there is any relevant stock or other purchase channels.