Bromine antimony flame retardant masterbatch

Catalog	ACMA00050962
Description	This product is a carrier-free bromine antimony flame retardant masterbatch with high bromine antimony content. It is processed through polymer activation and adopts a new low-temperature plasticizing and completely sealed production process.
Density	1.9±0.1 g/cm3
Application	1. It has efficient flame retardancy and thermal stability, good compatibility with resin, good processing and dispersion properties, and excellent mechanical properties. 2. It can effectively avoid dust pollution during the production process, and the product particles are uniform. 3. There is basically no loss during use, thereby reducing the consumption of raw materials. 4. All indicators comply with EU environmental protection requirements.
Storage	Products are stored in cool, dry conditions.
Apparent Density	1.5±0.1 g/cm3
Applicability	PA6, PA66 and other modified plastics.
Black Dot Rate	≦3pcs/100pcs
Color	White
Content	Bromine/Antimony 94.5% Other synergists 5.5%
Flammability	UL94 V-0 (1.6mm)
Flexural Strength	Formula 1 209 MPa Formula 2 205 MPa
Form	Granules
Formulation	Formula 1: PA66 31%, PA615%, BPS 18%, Sb2O3 5%, flame retardant 23%, GF 30%, other additives 1% Formula 2: PA66 31%, PA615%, flame retardant 23%, GF 30%, other additives 1%
Izod Impact-Notched	Formula 1 8.8 KJ/m2 Formula 2 8.6 KJ/m2
Moisture Content	≦0.1%
Particle Size	2-4 mm
Recommended Dosage	22-26%
Specific Gravity	Formula 1 1.61 g/cm3 Formula 2 1.58 g/cm3
Tensile Strength	Formula 1 160 MPa Formula 2 161 MPa

If the product of interest is not available in our catalog, please contact us to see if there is any relevant stock or other purchase channels.