Flame Retardant
- Halogen Flame Retardant
- Phosphorus Flame Retardant
- Nitrogen Flame Retardant
- Silicon Flame Retardant
- Aluminum-Magnesium Flame Retardant
- Antimony Flame Retardant
- Boron Flame Retardant
- Expandable Graphite
- MOF Flame Retardant
- Nano Flame Retardant
- Hyperbranched Polymer Flame Retardant
-
Functional Flame Retardant
- Composite Flame Retardant for PA
- Composite Flame Retardant for PP
- Composite Flame Retardant for PBT
- Composite Flame Retardant for PVC
- Composite Flame Retardant for PU
- Composite Flame Retardant for Silicone Rubber
- Composite Flame Retardant for Epoxy Resin
- Composite Flame Retardant for TPU
- Composite Flame Retardant for TPE
- Cotton Durable Flame Retardant
- Polyester Durable Flame Retardant
- Semi-durable Flame Retardant
- Non-durable Flame Retardant
- Others
- Smoke Suppressant
- Flame Retardant Polymer
- Flame Retardant Masterbatch
Flame Retardant ABS AF365S
Inquiry| Catalog | ACMA00051045 |
| Description | Product for extrusion and blow molding with flammability rating of V-0 at 2.0mm. |
| Application | Battery |
| Storage | Products are stored in cool, dry conditions. |
| Elongationat Break | 15%, (Min); 23℃, 50mm/min, 3.2mm |
| Elongation At Yield | 5%, (Min); 23℃, 50mm/min, 3.2mm |
| Feature | Flame retardancy, high flow, dimensional stability, and non-halogen properties. |
| Flammability | V-1 (1.7mm) V-0, 5VA (2.0mm) V-0, 5VA (2.5mm) V-0, 5VA (3.0mm) |
| Flexural Modulus | 2550 MPa (23℃, 10mm/min, 6.4mm) |
| Flexural Strength | 77 MPa (23℃, 10mm/min, 6.4mm) |
| HDT | 87℃ (Edgewise, 1.82MPa, 6.4mm, Unannealed) |
| Izod Impact-Notched | 290 J/m (3.2mm, 23℃) 200 J/m (6.4mm, 23℃) |
| Melt Flow Index | ASTM: 7.5 g/10min (220℃, 10kg) |
| Mold Shrinkage | ASTM: 0.4~0.7% (23℃, 3.2mm) |
| Rockwell Hardness | 108 (R-Scale) |
| Specific Gravity | ASTM: 1.16 (23℃) |
| Tensile Strength | 47 MPa (23℃, 50mm/min, 3.2mm) |