Flame Retardant
- Halogen Flame Retardant
- Phosphorus Flame Retardant
- Nitrogen Flame Retardant
- Silicon Flame Retardant
- Aluminum-Magnesium Flame Retardant
- Antimony Flame Retardant
- Boron Flame Retardant
- Expandable Graphite
- MOF Flame Retardant
- Nano Flame Retardant
- Hyperbranched Polymer Flame Retardant
-
Functional Flame Retardant
- Composite Flame Retardant for PA
- Composite Flame Retardant for PP
- Composite Flame Retardant for PBT
- Composite Flame Retardant for PVC
- Composite Flame Retardant for PU
- Composite Flame Retardant for Silicone Rubber
- Composite Flame Retardant for Epoxy Resin
- Composite Flame Retardant for TPU
- Composite Flame Retardant for TPE
- Cotton Durable Flame Retardant
- Polyester Durable Flame Retardant
- Semi-durable Flame Retardant
- Non-durable Flame Retardant
- Others
- Smoke Suppressant
- Flame Retardant Polymer
- Flame Retardant Masterbatch
MIL-100 (Cr)
InquiryCAS | 840523-88-8 |
Structure | |
Molecular Weight | 641.25 |
Molecular Formula | C18H10Cr3FO15 |
Appearance | Green Powder |
Storage | Store at room temperature or 4 °C in dry-state. Recommend to be activated at 150 ℃ in a vacuum oven for 3 hours before use |
Ligand | Trimesic acid (CAS: 554-95-0) |
Metal | Cr |
Pore Size | Window size: 0.55-0.88 nm; pore size: 2.5-2.9 nm |
Pore Volume | 0.9 cm³/g |
Size | 300-600 nm |
Specific Surface Area | 2000 m²/g (by BET) |
Stability | Thermal stability: > 300°C; Stable in air, aqueous and acid solution |
If the product of interest is not available in our catalog, please contact us to see if there is any relevant stock or other purchase channels.