Flame Retardant
- Halogen Flame Retardant
- Phosphorus Flame Retardant
- Nitrogen Flame Retardant
- Silicon Flame Retardant
- Aluminum-Magnesium Flame Retardant
- Antimony Flame Retardant
- Boron Flame Retardant
- Expandable Graphite
- MOF Flame Retardant
- Nano Flame Retardant
- Hyperbranched Polymer Flame Retardant
-
Functional Flame Retardant
- Composite Flame Retardant for PA
- Composite Flame Retardant for PP
- Composite Flame Retardant for PBT
- Composite Flame Retardant for PVC
- Composite Flame Retardant for PU
- Composite Flame Retardant for Silicone Rubber
- Composite Flame Retardant for Epoxy Resin
- Composite Flame Retardant for TPU
- Composite Flame Retardant for TPE
- Cotton Durable Flame Retardant
- Polyester Durable Flame Retardant
- Semi-durable Flame Retardant
- Non-durable Flame Retardant
- Others
- Smoke Suppressant
- Flame Retardant Polymer
- Flame Retardant Masterbatch
N-P Based Ammonium Polyphosphate Phase II For Fabric
Inquiry| CAS | 68333-79-9 |
| Molecular Formula | (NH4PO3)n n>1500 |
| Solubility | ≤0.5 (25℃, g/100ml) |
| Application | 1. Suitable for all types of flame-retardant textile coatings, especially for hot-water-stain-resistance acrylic emulsion coatings. 2. TF-212 is also suitable for other flame retardant fields that require higher water resistance and higher mechanical properties. 3. TF-212 works better in polyurethane emulsion, polyurethane glue, epoxy flame retardant and various resins. |
| Storage | in dry and cool place, keeping out of moisture and sunshine, shelf life two years. |
| Bulk Density | 0.9-1.1 g/cm³ |
| Content | P content 31% - 33%; N content ≥14% |
| Decomposition Temperature | ≥260℃ |
| Feature | no stain in hot warter |
| Moisture Content | ≤0.5% |
| Notes | Fireproof coating |
| Particle Size | about 18µm |