Flame Retardant
- Halogen Flame Retardant
- Phosphorus Flame Retardant
- Nitrogen Flame Retardant
- Silicon Flame Retardant
- Aluminum-Magnesium Flame Retardant
- Antimony Flame Retardant
- Boron Flame Retardant
- Expandable Graphite
- MOF Flame Retardant
- Nano Flame Retardant
- Hyperbranched Polymer Flame Retardant
-
Functional Flame Retardant
- Composite Flame Retardant for PA
- Composite Flame Retardant for PP
- Composite Flame Retardant for PBT
- Composite Flame Retardant for PVC
- Composite Flame Retardant for PU
- Composite Flame Retardant for Silicone Rubber
- Composite Flame Retardant for Epoxy Resin
- Composite Flame Retardant for TPU
- Composite Flame Retardant for TPE
- Cotton Durable Flame Retardant
- Polyester Durable Flame Retardant
- Semi-durable Flame Retardant
- Non-durable Flame Retardant
- Others
- Smoke Suppressant
- Flame Retardant Polymer
- Flame Retardant Masterbatch
NH2-UiO-66
Inquiry| CAS | 1260119-00-3 |
| Structure |  |
| Synonyms | UiO-66-BDC-NH2 |
| Molecular Weight | 1754.15 |
| Molecular Formula | C48H34N6O32Zr6 |
| Appearance | PaleYellow Powder |
| Storage | Store at room temperature or 4 °C in dry-state. Recommend to be activated at 150 ℃ in a vacuum oven for 3 hours before use |
| Ligand | 2-Aminoterephthalic acid (CAS: 10312-55-7) |
| Metal | Zr |
| Pore Size | 0.8 nm, 1.1 nm |
| Pore Volume | 0.5 cm³/g |
| Size | 300-600 nm |
| Specific Surface Area | 650-800 m²/g (by BET) |
| Stability | Thermal stability: > 400°C; Stable in aqueous and acid solution |