Flame Retardant
- Halogen Flame Retardant
- Phosphorus Flame Retardant
- Nitrogen Flame Retardant
- Silicon Flame Retardant
- Aluminum-Magnesium Flame Retardant
- Antimony Flame Retardant
- Boron Flame Retardant
- Expandable Graphite
- MOF Flame Retardant
- Nano Flame Retardant
- Hyperbranched Polymer Flame Retardant
-
Functional Flame Retardant
- Composite Flame Retardant for PA
- Composite Flame Retardant for PP
- Composite Flame Retardant for PBT
- Composite Flame Retardant for PVC
- Composite Flame Retardant for PU
- Composite Flame Retardant for Silicone Rubber
- Composite Flame Retardant for Epoxy Resin
- Composite Flame Retardant for TPU
- Composite Flame Retardant for TPE
- Cotton Durable Flame Retardant
- Polyester Durable Flame Retardant
- Semi-durable Flame Retardant
- Non-durable Flame Retardant
- Others
- Smoke Suppressant
- Flame Retardant Polymer
- Flame Retardant Masterbatch
UIO-66-COOH
Inquiry| Catalog | ACM1334722041-2 |
| CAS | 1334722-04-1 |
| Structure | ![{[CurrentData.Name]}](https://resource.alfa-chemistry.com/structure/1334722-04-1.gif) |
| Molecular Weight | 1928.12 |
| Molecular Formula | C54H22O44Zr6.H6 |
| Appearance | Off-White Powder |
| Storage | Store at room temperature or 4 °C in dry-state. Recommend to be activated at 150 ℃ in a vacuum oven for 3-5 hours before use |
| Ligand | Trimellitic Acid (CAS: 528-44-9) |
| Metal Content | Zr |
| Particle Size | 200-800 nm |
| Pore Size | 0.8 nm, 1.1 nm |
| Size | 200-800 nm |
| Specific Surface Area | 600-700 m²/g (by BET) |
| Stability | Thermal stability: > 350°C; Stable in aqueous and acid solution |
If the product of interest is not available in our catalog, please contact us to see if there is any relevant stock or other purchase channels.