Flame Retardant
- Halogen Flame Retardant
- Phosphorus Flame Retardant
- Nitrogen Flame Retardant
- Silicon Flame Retardant
- Aluminum-Magnesium Flame Retardant
- Antimony Flame Retardant
- Boron Flame Retardant
- Expandable Graphite
- MOF Flame Retardant
- Nano Flame Retardant
- Hyperbranched Polymer Flame Retardant
-
Functional Flame Retardant
- Composite Flame Retardant for PA
- Composite Flame Retardant for PP
- Composite Flame Retardant for PBT
- Composite Flame Retardant for PVC
- Composite Flame Retardant for PU
- Composite Flame Retardant for Silicone Rubber
- Composite Flame Retardant for Epoxy Resin
- Composite Flame Retardant for TPU
- Composite Flame Retardant for TPE
- Cotton Durable Flame Retardant
- Polyester Durable Flame Retardant
- Semi-durable Flame Retardant
- Non-durable Flame Retardant
- Others
- Smoke Suppressant
- Flame Retardant Polymer
- Flame Retardant Masterbatch
Unground and high whiteness Alumina Trihydrate (ATH), 75 μm
Inquiry| CAS | 21645-51-2 |
| Structure |  |
| Synonyms | Alumina trihydrate |
| Molecular Formula | Al(OH)3 |
| Purity | 0.996 |
| Appearance | White powder |
| Application | It is recommended for rubber goods, compression molded thermosets, adhesives, latex, vinyl and urethane compounds and carpet backings. |
| Storage | The product should be stored under dry and clean conditions in its original packing. The moisture content may increase if not stored under dry conditions. |
| Content | SiO2, <0.01% Fe2O3, <0.02% Na2O (total), 0.2 % Na2O (soluble), 0.2 % |
| Hardness | Moh’s Hardness 3.0 |
| Loss On Ignition | 550° C, 34.5% |
| Moisture Content | max 0.20% |
| Morphology | Hexagonal Platelets |
| Oil Absorption | 18 ml/100g |
| Packaging | 25 kg |
| Particle Size | 75 μm (Sedigraph 5100) 100 μm (Laser) |
| Specific Gravity | 2.42 g/cm³ |
| Specific Surface Area | 0.2 m3/g (BET) |
| Whiteness | Brightness Ry 90 |
If the product of interest is not available in our catalog, please contact us to see if there is any relevant stock or other purchase channels.