Flame Retardant
- Halogen Flame Retardant
- Phosphorus Flame Retardant
- Nitrogen Flame Retardant
- Silicon Flame Retardant
- Aluminum-Magnesium Flame Retardant
- Antimony Flame Retardant
- Boron Flame Retardant
- Expandable Graphite
- MOF Flame Retardant
- Nano Flame Retardant
- Hyperbranched Polymer Flame Retardant
-
Functional Flame Retardant
- Composite Flame Retardant for PA
- Composite Flame Retardant for PP
- Composite Flame Retardant for PBT
- Composite Flame Retardant for PVC
- Composite Flame Retardant for PU
- Composite Flame Retardant for Silicone Rubber
- Composite Flame Retardant for Epoxy Resin
- Composite Flame Retardant for TPU
- Composite Flame Retardant for TPE
- Cotton Durable Flame Retardant
- Polyester Durable Flame Retardant
- Semi-durable Flame Retardant
- Non-durable Flame Retardant
- Others
- Smoke Suppressant
- Flame Retardant Polymer
- Flame Retardant Masterbatch
ZIF-68
Inquiry| CAS | 1018477-09-2 |
| Structure |  |
| Synonyms | IRMOF-1 |
| Molecular Weight | 294.58 |
| Molecular Formula | C10H7N5O2Zn |
| Appearance | White Powder |
| Storage | Store at room temperature or 4 °C in dry-state. Recommend to be activated at 100 ℃ in a vacuum oven for 3 hours before use |
| Ligand | Terephthalic acid (CAS: 100-21-0) |
| Metal | Zn |
| Particle Size | 5-10 um rod crystals |
| Pore Size | 1.5 nm |
| Size | 200 nm; 500 nm; 1 µm; 5 µm |
| Specific Surface Area | 900 m²/g (by BET) |
| Stability | Thermal stability: > 300°C; Stable in air for several weeks, not stable in aqueous solution |
If the product of interest is not available in our catalog, please contact us to see if there is any relevant stock or other purchase channels.