Flame Retardant
- Halogen Flame Retardant
- Phosphorus Flame Retardant
- Nitrogen Flame Retardant
- Silicon Flame Retardant
- Aluminum-Magnesium Flame Retardant
- Antimony Flame Retardant
- Boron Flame Retardant
- Expandable Graphite
- MOF Flame Retardant
- Nano Flame Retardant
- Hyperbranched Polymer Flame Retardant
-
Functional Flame Retardant
- Composite Flame Retardant for PA
- Composite Flame Retardant for PP
- Composite Flame Retardant for PBT
- Composite Flame Retardant for PVC
- Composite Flame Retardant for PU
- Composite Flame Retardant for Silicone Rubber
- Composite Flame Retardant for Epoxy Resin
- Composite Flame Retardant for TPU
- Composite Flame Retardant for TPE
- Cotton Durable Flame Retardant
- Polyester Durable Flame Retardant
- Semi-durable Flame Retardant
- Non-durable Flame Retardant
- Others
- Smoke Suppressant
- Flame Retardant Polymer
- Flame Retardant Masterbatch
ZIF-90
Inquiry| Catalog | ACM1062147378-2 |
| CAS | 1062147-37-8 |
| Structure | ![{[CurrentData.Name]}](https://resource.alfa-chemistry.com/structure/1062147-37-8.gif) |
| Molecular Weight | 257.56 |
| Molecular Formula | C8H8N4O2.Zn |
| Appearance | Off-white/Grey Powder |
| Storage | Store at room temperature or 4 °C in dry-state. Recommend to be activated at 100 ℃ in a vacuum oven for 2 hours before use |
| Ligand | Imidazole-2-carboxaldehyde (CAS: 10111-08-7) |
| Metal Content | Zn |
| Particle Size | 500 nm |
| Pore Size | Window size: 0.35 nm; pore size: 1.1 nm |
| Pore Volume | 0.4 cm³/g |
| Size | 500 nm |
| Specific Surface Area | 1200 m²/g (by BET) |
| Stability | Thermal stability: ~300°C; Stable in air, aqueous and basic solution, not stable in acid solution |